data_PCOD3004939
_publ_section_title
;
Structure prediction by GRINSP 2.00 - 2006 (A. Le Bail)
SiO2           PCOD3004939 R =  0.0169
Probable space group: C M M 2
;
_chemical_formula_sum  "Si O2"
_cell_formula_units_Z   18
_cell_length_a         15.5912
_cell_length_b          7.9178
_cell_length_c         25.5093
_cell_angle_alpha     90.000
_cell_angle_beta      90.000
_cell_angle_gamma     90.000
_cell_volume          3149.09
_symmetry_space_group_name_H-M   "P 1"
_symmetry_Int_Tables_number  1
loop_
_symmetry_equiv_pos_as_xyz
x,y,z
loop_
_atom_site_label
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
Si1      0.41218  -0.00440   0.17736
Si2      0.60018   0.00355   0.17921
Si3      0.89480   0.50135   0.17844
Si4      0.08063   0.49946   0.18222
Si5     -0.00698   0.49339   0.07901
Si6      0.50902  -0.00448   0.07717
Si7     -0.00398  -0.17398   0.07646
Si8     -0.00299   0.16031   0.07733
Si9      0.49754   0.32541   0.07866
Si10      0.49623   0.66318   0.07776
Si11      0.15541  -0.18623   0.15583
Si12     -0.16845   0.18404   0.15205
Si13      0.15581   0.18560   0.15645
Si14     -0.17143  -0.18275   0.14992
Si15      0.66547   0.31699   0.15162
Si16      0.33314   0.68077   0.15209
Si17      0.66278   0.68738   0.15115
Si18      0.33508   0.31046   0.15447
O1      0.50553  -0.00144   0.20467
O2      0.42552  -0.00174   0.11464
O3      0.36235   0.16427   0.19551
O4      0.36327  -0.17629   0.19359
O5      0.59074   0.00125   0.11600
O6      0.64791   0.17564   0.19626
O7      0.64760  -0.17002   0.19564
O8      0.98624   0.50421   0.20767
O9      0.90874   0.49526   0.11564
O10      0.84779   0.32865   0.19546
O11      0.84392   0.67166   0.19322
O12      0.07314   0.49636   0.11889
O13      0.12795   0.32658   0.19876
O14      0.13035   0.67054   0.19827
O15     -0.00438   0.32872   0.04189
O16     -0.00531   0.65708   0.04157
O17      0.50607   0.16232   0.04104
O18      0.50713  -0.17140   0.04132
O19     -0.00324  -0.00576   0.04099
O20      0.07983  -0.17602   0.11314
O21     -0.08953  -0.17266   0.11180
O22     -0.08657   0.16671   0.11406
O23      0.08291   0.16799   0.11207
O24      0.49965   0.49363   0.04304
O25      0.58051   0.32707   0.11612
O26      0.40820   0.31611   0.10992
O27      0.40518   0.67206   0.10699
O28      0.57634   0.66757   0.11746
O29      0.16884  -0.00090   0.18074
O30      0.24281  -0.25361   0.12867
O31     -0.18696  -0.00027   0.17656
O32     -0.25209   0.24699   0.11984
O33      0.24444   0.24979   0.13035
O34     -0.25632  -0.24204   0.11819
O35      0.68499   0.50293   0.17475
O36      0.32518   0.49693   0.17893
#
#_symmetry_space_group_name_H-M  C M M 2
#_symmetry_Int_Tables_number   35
#
#   Coordination Sequence :
#
# PCOD3004939 SiO2            R =  0.0169   35
#   4
#   4  2  4  8
#    4   8  14  22  24  27  35  40  44   0
#    4   6  10  18  26  22  32  38  42   0
#    4   8  14  20  22  28  34  38  44   0
#    4  10  15  18  25  30  34  40  45   0
#
#_framework_density    5.72
#